High Chromium Cast Steel Ball

High Chromium Cast Steel Ball is made by introducing a fluid melt into a mold that is allowed to cool in the shape of a sphere. Four main elements are required in the casting process: the pattern, the mold, the core, and the partial pattern, from which the original template is prepared, created in the corresponding cavity of the casting material. The core is used to make the pipe or hole in the final die, and this part is the final output of the process. Casting can be used to form hot, liquid metals. The abrasive medium is heat treated to achieve the required combination of hardness, toughness and microstructure to ensure an excellent combination of wear resistance and toughness.

  Contact Now E-Mail Telephone WhatsApp
Product Details

Shandong jinchi heavy industry co., ltd. is a contemporary manufacturing corporation integrating r & d, production and sales!  The main products of the company are wear-resistant steel balls, wear-resistant steel rods, wear-resistant steel forgings, mill lining plates, steel structures, and mine accessories.   Excellent creates brand and fine creates blessings;   superior control standards, sophisticated system gadget, and tremendous personnel have applied the right excellent enchantment in each hyperlink of the production procedure, and found out the comprehensive upgrading of product nice.


Chromium Cast Steel Ball


  • High Chromium Cast Steel Ball parameters


Nominal diameter
(mm)

Weight of single ball  in average
(g)

Quantity/ MT

Surface hardness

Endurance impact test
(Times)

Φ15

13.8

72549

>60

>10000

Φ17

20.1

49838

>10000

Φ20

32.7

30607

>10000

Φ25

64

15671

>10000

Φ30

110

9069

>10000

Φ40

261

3826

>10000

Φ50

510

1959

>10000

Φ60

882

1134

>10000

Φ70

1401

714

>10000

Φ80

2091

478

>58

>10000

Φ90

2977

336

>10000

Φ100

4084

245

>8000

Φ120

7057

142

>8000

Φ130

8740

115

>8000


High Chromium Cast Steel Ball quality index


High Chromium Cast Steel Ball quality indicators:

Chromium content ≥10.0%, carbon content between 1.80%-3.20% are called high chromium ball, the national standard requirements of high chromium ball hardness (HRC) must be more than 58, impact value AK ≥3.0J/ 2, if the hardness of high chromium ball must use high temperature quenching + tempering treatment (at present domestic high chromium ball quenching oil quenching and wind quenching two quenching methods), If the test hardness (HRC) is below 54, the High chromium cast steel ball has not been quenched.

Chromium Cast Steel Ball


Manufacturing process flow chart of High Chromium Cast Steel Ball


Chromium Cast Steel Ball

Nominal diameter
(mm)

Weight of single ball  in average
(g)

Quantity/ MT

Surface hardness 

Endurance impact test
(Times)

Φ15

13.8

72549

>60

>10000

Φ17

20.1

49838

>10000

Φ20

32.7

30607

>10000

Φ25

64

15671

>10000

Φ30

110

9069

>10000

Φ40

261

3826

>10000

Φ50

510

1959

>10000

Φ60

882

1134

>10000

Φ70

1401

714

>10000

Φ80

2091

478

>58

>10000

Φ90

2977

336

>10000

Φ100

4084

245

>8000

Φ120

7057

142

>8000

Φ130

8740

115

>8000